TAWERS MAG Processes for Medium - Thick Material

Stable short-circuit progression with advanced weld-spatter control while maintaining high travel speeds  

Advantages:

• Stable arc
• Good penetration depths
• Material thickness: 2 - 6 mm
• Speed: 0.5 - 0.8 m/min

Patented pulse process in which a controlled drop discharge takes place. 

Advantages:

• Burn-in notches are reduced
• Good gap bridgeability
• Increased welding speed
• Welding from thick to thin / thin to thick
• Material thickness: 3 - 15 mm
• Speed: 0.3 - 0.8 m/min

The brazing process creates a flat and smooth weld.

Advantages:

• Low heat input prevents burn through
• Extremely low spatter across the current range
• Material thickness: 1 - 4 mm
• Speed: 0.5-0.8m/min

Zi-Tech is a process that can be used for low-spatter welding of galvanised components.

Advantages: 

• Prevents gas entrapment
• Reduction of adherent spatter
• Material thickness: 1 - 4 mm
• Welding speed: 0.5 - 0.8 m/min

Servo-controlled push-pull welding torch with special welding characteristics. 

Advantages: 

• High speed welding
• Extremely low spatter development
• Low heat input
• Material thickness: 1 - 6 mm
• Speed: 0.5 - 1.0 m/min (up to 3m/min in special layers)